Putty powder for interior wall: mainly used for leveling the surface of base material, generally not directly applied to the paint surface. During the construction, the whole batch shall be scraped 2-3 times, the first batch shall be repaired mainly, and the second batch shall be scraped flat without exposing the bottom. 2m aluminum alloy ruler can be scraped horizontally and then longitudinally to meet the requirements of straightness and verticality. After drying, polish the wall and remove the polishing dust. The dosage is about 2.5-4.0kg/m2. Putty powder for inner wall with smooth surface: it should be used together with leveling putty powder for inner wall to meet the requirements of smooth and delicate basic surface.

　　膩子粉的施工方法通常是分批涂(刮)涂，由于需要用量大，施工勞動強(qiáng)度也大，所以一定要有好的施工質(zhì)量，否則會直接影響膩子的使用。膩子粉的施工性能包括批刮和拋光。批刮是指膩子批刮手感柔軟、光滑、無粘稠感，刮板批背無卷邊，有適當(dāng)?shù)母稍飼r間，以便于對刮傷部位的缺陷進(jìn)行適當(dāng)?shù)男薷?良好的研磨性能是指膩子容易研磨光滑，研磨時不費力。

　　The construction method of putty powder is usually batch coating (scraping). Due to the large demand and the high labor intensity, it is necessary to have good construction quality, otherwise it will directly affect the use of putty. The construction performance of putty powder includes scraping and polishing. Scraping refers to the soft, smooth and non sticky feeling of putty scraping, no curling on the back of scraper scraping, and proper drying time, so as to facilitate the proper modification of the defects of the scraping parts; good grinding performance refers to the putty is easy to grind smooth and easy to grind.

　　平墻式內(nèi)墻在膩子粉施工時一般批量刮2次，每次厚度不超過0.5mm。干燥后，打磨墻面，清除拋光灰塵。用量約為1.2-1.5kg/m2。平面內(nèi)墻膩子粉:適用于普通場合，以滿足涂料裝飾工程對底面的一般要求。施工一般批量刮2次，每次厚度約1mm。干燥后，打磨墻面，清除拋光灰塵。用量約1.5-1.8kg/m2。注:一般拋光時間不宜過晚，約12-24小時為宜，過晚會影響拋光。

　　During the construction of putty powder, the flat wall type interior wall is generally scraped twice in batch, with the thickness not exceeding 0.5mm each time. After drying, polish the wall and remove the polishing dust. The dosage is about 1.2-1.5kg/m2. Putty powder for plane interior wall: it is suitable for ordinary occasions to meet the general requirements for the bottom surface of paint decoration engineering. Generally, the construction shall be scraped twice in batches, with a thickness of about 1mm each time. After drying, polish the wall and remove the polishing dust. The dosage is about 1.5-1.8kg/m2. Note: the general polishing time should not be too late, about 12-24 hours is appropriate, too late affects polishing.

　　有人認(rèn)為光澤性和膩子粉的理化性質(zhì)是一對矛盾,即膩子硬度高、物理化學(xué)性質(zhì)是好的,是不容易的光澤,和光澤容易的膩子硬度差,物理化學(xué)性質(zhì)性相對較低。這有一定道理，但不是全部。有些膩子可用于干燥后的膩子膜強(qiáng)度的時間差進(jìn)行拋光。也就是說，膩子薄膜表面已干燥，可在膩子強(qiáng)度(硬度)時進(jìn)行拋光，研磨時可提高極高。膩子粉易磨，但理化性能很好。

　　Some people think that the luster and the physical and chemical properties of putty powder are a pair of contradictions, that is, the hardness of putty is high, the physical and chemical properties are good, and the luster is not easy, and the hardness of putty with easy luster is poor, and the physical and chemical properties are relatively low. That makes sense, but not all. Some putty can be used for polishing the time difference of putty film strength after drying. That is to say, the surface of putty film is dry, and it can be polished when the strength (hardness) of putty is high, and it can be improved when grinding. Putty powder is easy to grind, but its physical and chemical properties are very good.

　　以上是濟(jì)南膩子粉廠家為大家介紹的相關(guān)內(nèi)容，想要了解更多內(nèi)容，歡迎訪問網(wǎng)站：http://www.sjzmx.cn

　　The above is the relevant content introduced by Jinan putty powder manufacturer. To learn more, please visit the website: http://www.sjzmx.cn