Ceramic tile sealant is powdered and powdered after seam construction, which is mainly caused by two aspects. First, in the early deployment of ceramic tile sealant paste, excessive water was added, and the composition of ceramic tile sealant binder was diluted by water, which could not form a compact and effective structure, and then appeared powder and powder. Another aspect is the construction of ceramic tile sealant filler, because water retention is a challenge, ceramic tile sealant lacks water hydration hardening reaction, the degree of hydration hardening will be limited, so the hardness and strength of the material will be affected, easy to appear material powder, powder problems.

　　瓷磚填縫施工之前,重要的是,當(dāng)部署瓷磚填縫劑泥漿,加水太多,也就是說,材料太稀疏,揭或混合材料時,沒有使用電動攪拌器,使材料不揭,或者前施工后剩下的瓷磚填縫劑泥漿干,加入水?dāng)嚢柚赜谩＿@三種做法，都會導(dǎo)致瓷磚填充劑出現(xiàn)起粉色、強度差的問題。

　　Before the ceramic tile filling construction, the most important thing is that when the tile filling agent slurry is deployed, too much water is added, that is to say, when the material is too sparse, uncovering or mixing materials, no electric mixer is used to keep the material uncovered, or the remaining ceramic tile filling agent slurry is dry before and after construction, and water mixing is added for reuse. These three methods will lead to the problems of pink and poor strength of ceramic tile filler.

　　另外，瓷磚補縫劑實際上就是補縫施工后的蓄水、保水、保濕、鎖水的能力。當(dāng)磚縫太小時，用瓷磚填充縫劑填充縫隙時，材料的寬度很小，即材料的體積較小。體積小不利于堵縫材料的保水性，易被瓷磚吸收空氣中的水分，導(dǎo)致瓷磚堵縫劑粉體問題;此外，瓷磚密封膠填補縫隙，如果填料不飽滿、不致密、疏松，瓷磚密封膠之間的縫隙很容易流失水分。這就導(dǎo)致瓷磚填充縫料漿在硬化過程中缺水，容易出現(xiàn)粉狀，硬度不夠;在如果天氣太干太熱,瓷磚密封膠施工很容易被吸走空氣水分,導(dǎo)致缺乏水淬火條件下,會出現(xiàn)粉、硬度不夠,所以當(dāng)天氣熱或干燥的天氣,噴水維護、合適的潤濕材料的一個重要原因。

　　In addition, the ceramic tile sealant is actually the ability to store, retain, moisturize and lock water after the construction of the seam. When the brick seam is too small and the ceramic tile filling agent fills the seam, the width of the material is very small, that is, the volume of the material is small. Small size is not conducive to the water retention of sealing materials, easy to be absorbed by ceramic tiles in the air moisture, leading to the problem of ceramic tile sealant powder; in addition, ceramic tile sealant fills the gap, if the filler is not full, compact, loose, the gap between ceramic tile sealants is easy to lose moisture. This will lead to the lack of water in the hardening process of ceramic tile filling seam slurry, which is easy to appear powdery and hardness is not enough; if the weather is too dry and hot, the construction of ceramic tile sealant is easy to absorb air moisture, resulting in lack of water quenching conditions, there will be powder, hardness is not enough, so when the weather is hot or dry, spray water maintenance, appropriate moistening. An important reason for wet materials.

　　為了防止瓷磚填縫劑發(fā)生粉變化,粉紅色的情況下,在分配瓷磚填縫劑泥漿在早期,添加水的量要適當(dāng),不能太多,當(dāng)瓷磚填縫劑后的后期建筑保護,水分不能少,應(yīng)注意材料填滿水。

　　In order to prevent the powder change of ceramic tile sealant and pink, in the early stage of distributing ceramic tile sealant slurry, the amount of water should be appropriate and not too much. When the later stage of building protection after ceramic tile sealant, the water should not be less, and the material should be filled with water.

　　以上內(nèi)容由濟南抹面砂漿廠家整理發(fā)布，如果您不了解這方面的裝飾材料或有產(chǎn)品需求可以點擊官網(wǎng)咨詢:http://www.sjzmx.cn/

　　The above contents are arranged and published by Jinan Gypsum Mortar Manufacturer. If you don't know the decorative materials or product requirements in this area, you can click on the official website to consult: http://www.sjzmx.cn./