石膏粉是一種廣泛應(yīng)用在建筑、藝術(shù)制作等領(lǐng)域的材料。它主要由石膏礦物和適量的助劑混合制成。在制作石膏粉的過程中，需要進行碾磨、煅燒、冷卻、篩分等步驟。

Gypsum powder is a widely used material in fields such as architecture and artistic production. It is mainly made by mixing gypsum minerals with an appropriate amount of additives. In the process of producing gypsum powder, steps such as grinding, calcination, cooling, and screening are required.

石膏礦物的選取

Selection of gypsum minerals

選擇好的石膏礦物作為原料是石膏粉制作的首要步驟。在選取石膏礦物時需要考慮其成分、質(zhì)地和純度。常用的石膏礦物有石膏石、蒸發(fā)石膏、膨潤土石膏等。其中，石膏石是常用的原料。

Choosing good gypsum minerals as raw materials is the primary step in the production of gypsum powder. When selecting gypsum minerals, it is necessary to consider their composition, texture, and purity. Common gypsum minerals include gypsum stone, evaporated gypsum, bentonite gypsum, etc. Among them, gypsum stone is a commonly used raw material.

碾磨

Grinding

將選取的石膏礦物送入碾磨機中進行碾磨處理，將塊狀的石膏礦物磨成細粉末。碾磨機的選用要考慮石膏礦物的硬度和韌性，一般使用球磨機或者離心磨機。

Send the selected gypsum minerals into a grinding mill for grinding treatment, and grind the block like gypsum minerals into fine powder. The selection of grinding machines should consider the hardness and toughness of gypsum minerals, usually using ball mills or centrifugal mills.

篩分

screening

將碾磨好的石膏粉末進行篩分處理，去除粉末中的雜質(zhì)和大顆粒。篩分后的石膏粉末需要達到一定的細度和均勻度要求。

Screen and treat the ground gypsum powder to remove impurities and large particles from the powder. The screened gypsum powder needs to meet certain requirements for fineness and uniformity.

煅燒

calcination

將篩分后的石膏粉末送入煅燒窯內(nèi)進行煅燒處理。煅燒過程中，石膏粉末會逐漸變硬，水分會被蒸發(fā)掉，同時石膏中的各種雜質(zhì)也會被分解和揮發(fā)。煅燒溫度一般在160℃到200℃之間，時間取決于石膏粉末的成分和燒結(jié)要求。

Send the screened gypsum powder into the calcination kiln for calcination treatment. During the calcination process, gypsum powder will gradually harden, water will be evaporated, and various impurities in gypsum will also be decomposed and evaporated. The calcination temperature is generally between 160 ℃ and 200 ℃, and the time depends on the composition of gypsum powder and sintering requirements.

冷卻

cooling

煅燒后的石膏塊需要進行冷卻處理，防止熱量對石膏粉末的影響。冷卻方式可以使用風冷或者水冷方式。

The calcined gypsum blocks need to be cooled to prevent the influence of heat on the gypsum powder. The cooling method can be air cooling or water cooling.

粉碎

smash

將冷卻后的石膏塊送入粉碎機中進行二次研磨，將石膏塊研磨成粉末。這個過程中需要控制粉碎機的轉(zhuǎn)速和拍打次數(shù)。

Send the cooled gypsum block into the crusher for secondary grinding, and grind the gypsum block into powder. During this process, it is necessary to control the speed and number of beats of the crusher.

加入助劑

Adding additives

為了提高石膏粉末的質(zhì)量和性能，在粉末中適量加入一些助劑，如凝結(jié)劑、流動劑等。這些助劑可以改變石膏粉末的物理性質(zhì)和化學性質(zhì)，提高石膏粉末的強度和流動性。

In order to improve the quality and performance of gypsum powder, some additives such as coagulants and flowers are added in an appropriate amount to the powder. These additives can change the physical and chemical properties of gypsum powder, improve its strength and flowability.

包裝

packing

將加入助劑后的石膏粉末裝入袋內(nèi)，密封保存。在包裝時需要注意石膏粉末的濕度和容量，以避免粉末受潮和過度壓縮。

Put the gypsum powder added with additives into a bag and seal it for storage. When packaging, it is necessary to pay attention to the humidity and capacity of gypsum powder to avoid moisture and excessive compression of the powder.